Description
DEKAsyl MS-2 is the ideal compromise between adhesive and sealant for the creation of elastic connections between components that also require high adhesive strength.
DEKAsyl MS-2 bonds and seals in one and does not weaken the material used and leaves no traces of joining elements (screws or similar).
It is possible to recoat the MS-2 adhesive sealant after skin formation.
The areas of application and use are varied and can be extended as required.
Colour: Grey
content: 290 ml
Packaging: Cartridge
areas of application:
– Aluminium
– Polysester
– CSF
– PMMA
– Compensation of building tolerances
– Glass
– Skylights – and windows
– Wheel fairings
– and much more
Technical data:
Base material: MS Polymer
Cure/ sealing: moisture
Specific gravity: approx. 1.4 Kg/litre
Skin formation time (20°C/50% rel. LF): approx. 10 minutes
Open time (20°C/50% relative humidity): < 15 minutes
Curing after 24 h (20°C/50% relative humidity): approx. 3 mm
Shore A hardness (DIN 53505): approx. 55
Volume change (DIN 52451): < 3%.
Adhesion strength (Physical Rheometer MC100): approx.300 Pa
(Measure for the maximum amount of adhesive that can be applied per m² without running down)
Tensile stress (100%) (DIN 53504/ISO 37): approx. 1.7 MPa
Tensile stress at break (DIN 53504/ISO 37): approx. 2.6 MPa
Elongation at break (DIN 53504/ISO 27): approx. 250%.
Shear stress (DIN 53283/ASTM D1002): approx. 2.5 MPa
Tear resistance (DIN 53515/ISO 34): approx. 16 N/mm
Solvent content: 0%.
Isocyanate content: 0%.
Temperature resistance : -40°C to +120°C
Application temperature : +5°C to +35°C
UV and weathering resistance: excellent